Available materials for DMLS technology

We keep track of  whole production process in order to fulfill the highest quality standards for manufactured parts.

Basic mechanical properties of available DMLS Materials
	Tensile strength	Yield strength	Young’s modulus	Elongation at break	Hardness
MS1 (1.2709)*	2050 ±100 MPa	1990 ±100 MPa	180 ±20 GPa	4 ±2 %	50-56 HRC